b) Choosing and preparing the electrode
- The electrodes normally used are of cerium tungsten (2% cerium, grey in colour)
and the following diameters are recommended depending on the current:
- A tip is made on the electrode as shown in the figure.
- Angle a
welding
varies; the following table recommends the value:
Angle (°)
30
60 – 90
90 –120
c) Weld material
- Many kinds of materials may be treated, however there are some basic rules
1 )
the rods of weld material must have the same mechanical and chemical
properties as the material to be welded
2) it is recommended not to use parts of the base material, as they could contain
impurities due to the work process ;
3) if the material used has a different chemical composition, it is advisable to
assess the final characteristics of the joint, both mechanical and anti-corrosive.
d) Protection gas
- The protection gas normally used is pure argon with a quantity that varies
according to the current used (4-6 I/min).
- The TIG process is indicated for welding steel (both carbon steel and alloys), it
gives a weld with an excellent appearance which limits subsequent processing and
is often used for the first pass on pipes.
- Before every weld it is necessary to perform accurate preparation and cleaning of
STEL s.r.l. – Via del Progresso n° 59 – 36020
Loc. Castegnero (VICENZA) - ITALY
TEL. +39 444 639525 (central.) – +39 444 639682 (comm.)
FAX +39 444 639641 – E-mail:stelgroup.com
http: www.stelgroup.it
TECHNICAL DESCRIPTION
varies as the
current
Welding current A
5 - 30
30 - 120
120 - 160
;
ENGLISH
b) Choosing and preparing the electrode
- The electrodes normally used are of cerium tungsten (2% cerium, grey in colour)
and the following diameters are recommended depending on the current:
- A tip is made on the electrode as shown in the figure.
- Angle a
welding
varies; the following table recommends the value:
c) Weld material
: - Many kinds of materials may be treated, however there are some basic rules
1 )
the rods of weld material must have the same mechanical and chemical
properties as the material to be welded
2) it is recommended not to use parts of the base material, as they could contain
impurities due to the work process
3) if the material used has a different chemical composition, it is advisable to
assess the final characteristics of the joint, both mechanical and anti-corrosive.
d) Protection gas
- The protection gas normally used is pure argon with a quantity that varies
according to the current used (4-6 I/min).
- The TIG process is indicated for welding steel (both carbon steel and alloys), it
gives a weld with an excellent appearance which limits subsequent processing and
is often used for the first pass on pipes.
- Before every weld it is necessary to perform accurate preparation and cleaning of
STEL s.r.l. – Via del Progresso n° 59 – 36020
Loc. Castegnero (VICENZA) - ITALY
TEL. +39 444 639525 (central.) – +39 444 639682 (comm.)
FAX +39 444 639641 – E-mail:stelgroup.com
65 http: www.stelgroup.it
TIG µP 353H DC
COD. 6903700030
Angle (°) Welding current A
30
60 – 90
90 –120
;
;
TECHNICAL DESCRIPTION
varies as the
current
5 - 30
30 - 120
120 - 160
:
65