- Due to the properties already described, TIG welding is also excellent for working
on materials with high heat conductivity. The gas used is always argon and, in the
case of copper, the use of a reversed support is recommended.
- Preparation of the edges for welding copper (flat butt joint).
- The electrode used is of the same type described for welding steel; it is prepared
as described above.
s (mm) a (mm)
1÷3 0
4÷10 0
4÷10 0
- To avoid possible oxidation in the welded area, weld materials containing
phosphor, silicon and deoxidizing components are used.
WELDING ALUMINIUM
– Due to the properties already described, TIG welding is also excellent for
working on aluminium. The gas used is always argon (or helium).
- For preparation of the edges, see the guide table on the next page.
- The electrode must be of cerium tungsten; it is prepared as described above.
STEL s.r.l. – Via del Progresso n° 59 – 36020
Loc. Castegnero (VICENZA) - ITALY
TEL. +39 444 639525 (central.) – +39 444 639682 (comm.)
FAX +39 444 639641 – E-mail:stelgroup.com
http: www.stelgroup.it
TECHNICAL
DESCRIPTION
d (mm) α(°)
0 0
1-s/4 0
0 60÷90
65
ENGLISH
TIG µP 203H-353H AC/DC
COD. 6902500070
TIG WELDING ON COPPER
- Due to the properties already described, TIG welding is also excellent for working
on materials with high heat conductivity. The gas used is always argon and, in the
case of copper, the use of a reversed support is recommended.
- Preparation of the edges for welding copper (flat butt joint).
- The electrode used is of the same type described for welding steel; it is prepared
as described above.
s (mm) a (mm)
1÷3 0
4÷10 0
4÷10 0
- To avoid possible oxidation in the welded area, weld materials containing
phosphor, silicon and deoxidizing components are used.
WELDING ALUMINIUM
– Due to the properties already described, TIG welding is also excellent for
working on aluminium. The gas used is always argon (or helium).
- For preparation of the edges, see the guide table on the next page.
- The electrode must be of cerium tungsten; it is prepared as described above.
STEL s.r.l. – Via del Progresso n° 59 – 36020
Loc. Castegnero (VICENZA) - ITALY
TEL. +39 444 639525 (central.) – +39 444 639682 (comm.)
FAX +39 444 639641 – E-mail:stelgroup.com
http: www.stelgroup.it
TECHNICAL
DESCRIPTION
d (mm) α(°)
0 0
1-s/4 0
0 60÷90
65